TY - JOUR
T1 - Effect of high-power-laser with and without graphite coating on bonding of resin cement to lithium disilicate ceramic
AU - Feitosa, Fernanda A.
AU - De Araújo, Rodrigo M.
AU - Tay, Franklin R.
AU - Niu, Lina
AU - Pucci, César R.
N1 - Funding Information:
The authors thank the support from Fapesp Proc 2013/02953-5 and 2012/08443-6, and grant 2015QNRC001 from Young Elite Scientist Sponsorship Program by CAST.
Publisher Copyright:
© 2017 The Author(s).
PY - 2017/12/1
Y1 - 2017/12/1
N2 - The present study evaluated the effect of different high-power-laser surface treatments on the bond strength between resin cement and disilicate ceramic. Lithium disilicate ceramic specimens with truncated cones shape were prepared and divided into 5 groups: HF (hydrofluoric acid-etching), Er:YAG laser + HF, Graphite + Er:YAG laser + HF, Nd:YAG laser + HF, and Graphite + Nd:YAG laser + HF. The treated ceramic surfaces were characterized with scanning electron microscopy and surface roughness measurement. Hourglasses-shaped ceramic- resin bond specimens were prepared, thermomechanically cycled and stressed to failure under tension. The results showed that for both the factors "laser" and "graphite", statistically significant differences were observed (p < 0.05). Multiple-comparison tests performed on the "laser" factor were in the order: Er:YAG > Nd:YAG (p < 0.05), and on the "graphite" factor were in the order: graphite coating < without coating (p < 0.05). The Dunnett test showed that Er:YAG + HF had significantly higher tensile strength (p = 0.00). Higher surface roughness was achieved after Er:YAG laser treatment. Thus Er:YAG laser treatment produces higher bond strength to resin cement than other surface treatment protocols. Surface-coating with graphite does not improve bonding of the laser-treated lithium disilicate ceramic to resin cement.
AB - The present study evaluated the effect of different high-power-laser surface treatments on the bond strength between resin cement and disilicate ceramic. Lithium disilicate ceramic specimens with truncated cones shape were prepared and divided into 5 groups: HF (hydrofluoric acid-etching), Er:YAG laser + HF, Graphite + Er:YAG laser + HF, Nd:YAG laser + HF, and Graphite + Nd:YAG laser + HF. The treated ceramic surfaces were characterized with scanning electron microscopy and surface roughness measurement. Hourglasses-shaped ceramic- resin bond specimens were prepared, thermomechanically cycled and stressed to failure under tension. The results showed that for both the factors "laser" and "graphite", statistically significant differences were observed (p < 0.05). Multiple-comparison tests performed on the "laser" factor were in the order: Er:YAG > Nd:YAG (p < 0.05), and on the "graphite" factor were in the order: graphite coating < without coating (p < 0.05). The Dunnett test showed that Er:YAG + HF had significantly higher tensile strength (p = 0.00). Higher surface roughness was achieved after Er:YAG laser treatment. Thus Er:YAG laser treatment produces higher bond strength to resin cement than other surface treatment protocols. Surface-coating with graphite does not improve bonding of the laser-treated lithium disilicate ceramic to resin cement.
UR - http://www.scopus.com/inward/record.url?scp=85037848853&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85037848853&partnerID=8YFLogxK
U2 - 10.1038/s41598-017-17808-x
DO - 10.1038/s41598-017-17808-x
M3 - Article
C2 - 29234138
AN - SCOPUS:85037848853
SN - 2045-2322
VL - 7
JO - Scientific reports
JF - Scientific reports
IS - 1
M1 - 17422
ER -